| 牌號 | Cu% | Sn % | Zn % |
| FDCuSn10 | 88~91 | 其余 | |
| FDCuSn 15 | 78~81 | 其余 | |
| FDCuSn 20 | 68.5~71.5 | 其余 | 0 |
| FDCuSn6Zn6 | 余量 | 5~7 | 5~7 |
| 牌號 | 規格 | 粒徑組成(質量分數)/% |
松裝密度 g/cm3 |
流動性 s/50g |
|||
| ≥150μm | 150μm~75μm | 75μm～45μm | ≤45μm | ||||
| FDCuSn10 | 150μm | ≤3 | 20~30 | 30~40 | ≤55 | 2.0~2.6 | ≤45 |
| 75μm | ≤3 | 15~35 | ≥65 | 2.0~2.8 | ≤45 | ||
| 45μm | — | ≤3 | ≥97 | 2.4~2.6 | |||
| FDCuSn15 | 150μm | ≤3 | 20~30 | 30~40 | ≤55 | 2.0~2.6 | ≤45 |
| 75μm | ≤3 | 15~35 | ≥65 | 2.0~2.8 | ≤45 | ||
| 45μm | ≤3 | ≥97 | 2.4~2.6 | ||||
| FDCuSn20 | 150μm | ≤3 | 20~30 | 30~40 | ≤55 | 2.0~2.6 | ≤45 |
| 74μm | ≤3 | 15~35 | ≥65 | 2.0~2.8 | ≤45 | ||
| 45μm | ≤3 | ≥97 | 2.4~2.6 | ||||
| FDCuSn6Zn6 | 150μm | ≤3 | 20~30 | 30~40 | ≤55 | 2.0~2.6 | ≤45 |
| 74μm | ≤3 | 15~35 | ≥65 | 2.0~2.8 | ≤45 | ||
| 45μm | ≤3 | ≥97 | 2.4~2.6 | ||||
| 化學成分(質量分數)/% | ||||||||
|
Cu+Sn+Zn
不 于
|
雜質(不大于) | |||||||
| 99.5 | Fe | Pb | As | Cd | Hg | Cr | 0 | 總和 |
| 0.05 | 0.05 | 0.005 | 0.005 | 0.005 | 0.005 | 0.1 | 0.5 | |
|
注1:如需方對產品化學成分有特殊要求，由供需雙方協商。 注2:化學成分中不包括添加劑，如加添加劑，標明所加添加劑名稱和添加量。 |
||||||||
| 產品牌號 | 燒結收縮率 96 | 松裝密度 g/cm |
流動性 s/50s |
壓縮性 g/cm° |
生坯強度 (MPa) |
徑向壓潰強度 (MPa) |
| FDCuSn10 | 1.2~1.4 | 2.2~3.0 | <45 | >7.2 | >8 | >180 |
| FDCuSn15 | 1.4~1.6 | 2.2~3.0 | <45 | >7.2 | >8 | >160 |
| FDCuSn20 | 1.4~1.6 | 2.2~3.0 | <45 | >7.2 | >8 | >160 |
| FDCuSn6Zn6 | 1.2~1.4 | 2.2~3.0 | <45 | >7.2 | >8 | >180 |
| 備注：測試收縮率的條件，壓制密度6.2g/cm3,350攝氏度下預氧化脫蠟30min,在700℃下燒結30min | ||||||